离子型聚乙烯醇海绵的结构及性能 |
| |
孙瑞焕 毛立江 胡元洁 张颖 王青 朴东旭
摘要： 以聚乙烯醇(PVA)为原料，采用缩醛化、发泡成型、接枝聚合 的方法，制造了多孔泡沫海绵状吸液材料：离子化聚乙烯醇海绵(i-PVA海绵)。结构分析表 明，i-PVA海绵具有三维多孔织构，由于引入了大量的阴离子基团，i-PVA海绵具有优异的 吸液性能。临床使用证明，i-PVA海绵可用于白内障复明手术中的特殊用途。
关键词： 离子化聚乙烯醇海绵；吸液性能；三维多孔织构；白内障复明
中图分类号：R496 文献标识码：A 文章编号：1006-9771(2000)02-0056-03
Structure and properties of ionic PVA sponges
SUN Ruihuan,MAO L ijing,HU Yuanjie,et al
(Chinese Journal of Rehabilitation Theory & Practice)
Abstract: A new kind of medical sponges,ionic polyvi nyl alcohol sponges(i-PVA sponges)were prepared by surface-grafting of acrylic acid onto acetal-PVA sponges.i-PVA sponges obtained show excellent hydrophili city and water-absorption.The i-PVA sponges are three dimentional porous netwo rk.Because there are great amount of carboxyl and sodium carboxylate groups on P VA molecule chains,the speed of water absorption and water-absorptivity is ＞2. 9mm/s and ＞15 times respectively.That is,in the case of the cataract-extractio n,the polyion-modified sponges much more advantageous than any traditional noni onic polymer sponges.
Key words: ionic polyvinyl alcohol sponges;water-ab sorption;three dimentional porous network;cataract-extraction
1 前言
采用化学合成方法制造的医用海绵在许多手术中已经取代了传统的医用脱脂棉。特别在眼科 、耳鼻喉科及显微外科手术中，这类医用海绵已成为必用材料［1］。但是这类医用 海绵都是由纯的纤维素、PVA等非离子性高分子制成的；为了配合国家卫生部和中国残疾人 联合会在全国实施的“白内障复明康复计划”，我们较系统地进行了白内障复明手术用医用 海绵材料的研究。我们曾研究了离子络合纤维聚集而成的高分子海绵［2～3］。在这 种纤维型海绵研究成功并产业化的基础上，我们又研究成功了非纤维型医用海绵。这种新型 海绵是在聚乙烯醇大分子上引入聚丙烯酸钠侧链而成的，我们称之为离子化聚乙烯醇海绵( 简称i-PVA海绵)，是一种非纤维多孔结构，生物相容性良好，化学性能稳定，具有优良的 亲水、吸液、吸血性能。本文就这种新型医用海绵的结构特征及性能特点进行讨论。
2 实验
2.1 原料及合成方法
聚乙烯醇(1799)，铈盐催化剂，酸碱助剂，丙烯腈。
采用北京康安高分子研究开发中心生产的聚乙烯醇缩醛化发泡体为原料，在铈盐催化作用下 ，进行非均相接枝反应，将丙烯睛接枝在聚乙烯醇。反应产物用酸及碱助剂处理，得到聚乙 烯醇多孔海绵体。
2.2 试验
2.2.1 结构分析、织构形态观察
用红外光谱法(IR)和示差扫描量热法(DSC)测试样品，分析材料化学、物理结构。用扫描电 镜观察样品的织构形态。
2.2.2 吸液性能试验
分别测定聚乙烯醇海绵对去离子水、生理盐水、人工尿、酸、碱溶液的吸液速度[1] [2] 下一页